Composites of bovine hydroxyapatite (BHA) and ZnO

Basit öğe sayfası
dc.contributor.authorGunduz, Oguzhan
dc.contributor.authorErkan, Eray M.
dc.contributor.authorDaglilar, Sibel
dc.contributor.authorSalman, Serdar
dc.contributor.authorAgathopoulos, Simeon
dc.contributor.authorOktar, Faik Nuzhet
dc.contributor.institutionauthorDAĞLILAR, Sibel
dc.date.accessioned2026-06-27T13:09:51Z
dc.date.issued2008
dc.description.abstractComposites of calcinated bovine bone-derived hydroxyapatite (BHA), doped with 2.5, 5, and 10 wt.% ZnO were produced by sintering. Scanning electron microscopy (SEM) and X-ray diffraction analysis together with measurements of density, compressive strength, and Vickers microhardness were carried out in the sintered samples. The experimental results showed that the best mechanical properties were achieved in the samples with 5% addition of ZnO. The highest value of compression strength was achieved after sintering at 1200 degrees C (72 MPa) and of microhardness at 1300 degrees C (548 HV). Prolong heat treatment at 1300 degrees C results in vulnerable BHA-ZnO composites to over-firing effect.en
dc.description.urihttps://doi.org/10.1007/s10853-008-2497-1
dc.identifier.doi10.1007/s10853-008-2497-1
dc.identifier.eissn1573-4803
dc.identifier.endpage2540
dc.identifier.issn0022-2461
dc.identifier.issue8
dc.identifier.startpage2536
dc.identifier.urihttps://hdl.handle.net/20.500.14981/50607
dc.identifier.volume43
dc.identifier.wos000254249900003
dc.language.isoeng
dc.publisherSPRINGER
dc.relation.ispartofJOURNAL OF MATERIALS SCIENCE
dc.subjectMECHANICAL-PROPERTIES
dc.subjectSINTERING TEMPERATURE
dc.subjectZINC RELEASE
dc.subjectGLASS
dc.subjectENAMEL
dc.subjectMaterials Science
dc.titleComposites of bovine hydroxyapatite (BHA) and ZnO
dc.typeArticle
dspace.entity.typePublication
local.import.sourceWOS

Dosyalar

Koleksiyonlar

Yayınlar