The effect of holding time after Sr addition on microstructural and mechanical properties of A356 alloy

Abstract

The spheroidization of the silicon eutectic phase in aluminum is an important parameter for casting and significantly influences the material properties. Sr has been used for a long time for eutectic modification in aluminum and many researches have been made on this subject. In this study, the effect of holding time after Sr addition on the mechanical properties and eutectic phase modification of the aluminum were investigated. 200 ppm Sr was chosen as the amount of Sr and the holding times were chosen as 20, 40 and 80 minutes. Tensile test was performed for the determination of mechanical properties and ultimate tensile strength and percentage of elongation values were measured. In order to quantify eutectic eutectic modification, the length/width (aspect ratio) ratios of eutectic silicon particles were measured. In addition, Bifilm Index of the molten metal was determined with the reduced pressure test (RPT). With the increase in the holding time, an increase in the aspect ratio and in the Bifilm Index was measured. It has been observed that the tensile strength and elongation values have decreased as the holding time has increased.