Microbiologically influenced corrosion of galvanized steel by Desulfovibrio sp and Desulfosporosinus sp in the presence of Ag-Cu ions

Abstract

The effects of Ag-Cu ions on the microbiologically induced corrosion of galvanized steel in the presence of Desulfovibrio sp. and Desulfosporosinus sp. were investigated. The corrosion behavior of galvanized steel was analyzed by potentiodynamic polarization and electrochemical impedance spectroscopy. The biofilm, corrosion products and Ag-Cu ions on the surfaces were investigated by using scanning electron microscopy, energy dispersive X-ray spectrometry and elemental mapping. The biofilm layer formed by the Desulfovibrio sp. was stable covering the all surface of galvanized steel coupons, while that by Desulfosporosinus sp. was intermittent, highly porous and heterogeneous. It was found that both of the sulfate reducing bacteria species accelerated corrosion of the galvanized steel. However, it was detected that Desulfosporosinus sp. was more corrosive for galvanized steel than Desulfovibrio sp. Scanning electron microscopy images showed that Desulfovibrio sp. and Desulfosporosinus sp. in biofilm clustered into patches on the galvanized steel surface when the culture contained toxic Ag-Cu ions. The ions affected the growth of the sulfate reducing bacteria strains in different ways and hence the corrosion behaviors. It was observed that the Ag-Cu ions affected negatively growth of Desulfosporosinus sp. especially after 24 h of exposure leading to a decrease in the corrosion rate of galvanized steel. However, Desulfovibrio sp. showed more corrosive effect in the presence of the ions according to the ions-free culture. Energy dispersive X-ray spectrometry analysis showed that corrosion products on the surfaces were mainly composed of Zn, S, Na, O and P. (C) 2015 Elsevier B.V. All rights reserved.